2024 | OriginalPaper | Buchkapitel

3. Conditions for Appearance of Internal Intergranular Cracking Type Fracture Under Creep-Fatigue

verfasst von : Weisheng Zhou, Naoya Tada, Junji Sakamoto

Erschienen in: Creep-Fatigue Fracture: Analysis of Internal Damage

Verlag: Springer Nature Singapore

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

This Chapter presents analytical results based on the experimental results and observations of cracks in creep-fatigue tests of a stainless steel SUS304. Two fracture morphologies were observed in high-temperature creep-fatigue fracture: inner cracking type fracture due to coalescence of small internal intergranular cracks and surface cracking type due to growth of small surface intergranular cracks. The fracture morphologies are strongly dependent on loading conditions. The inner cracking type fracture occurs at low tensile strain rate and high compressive strain rate, as well as at high temperatures, on the other hand, the surface cracking type fracture occurs under the opposite conditions. Three-dimensional fracture mechanism maps were created for tensile strain rate, compressive strain rate, and temperature to visualize the relationship between loading conditions and fracture morphologies. For the same strain range at high temperatures, the fatigue life at fatigue cracking type fracture is the longest, followed by the fatigue life at surface intergranular cracking type fracture and the fatigue life at internal intergranular cracking type fracture.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Grain Boundary Cavity and Damage Evaluation in Creep-Fatigue

Nächstes Kapitel Initiation and Growth Behavior of Small Inner Crack

F. Garofalo, Fundamentals of Creep and Creep-Rupture in Metals (Macmillan, 1965)

S. Taira, R. Ohtani, High-temperature Strength of Materials (Ohmsha, 1980) (in Japanese).

R. Ohtani, K. Komai, Kankyou kouon kyoudogaku. Sougou zairyou kyoudogaku kouza, Ohmsha 7, 177–346 (1984). ((in Japanese))

M. E. Evans, Mechanism of Creep Fracture (Elsevier Applied Science Publishers, 1984), pp. 15–25

S. Usami, Y. Fukuda, S. Shida, Micro-crack initiation and propagation in 304 stainless steel plain specimen under fatigue-oxidation interaction at elevated temperature. J. Soc. Mat. Sci., Jpn. 33(369), 685–691 (1984) (in Japanese)

R. Ohtani, T. Kinami, H. Sakamoto, Small crack propagation in high temperature creep-fatigue of 304 stainless steel. Trans. Jpn. Soc. Mech. Eng. Ser. A 52(480), 1824–1830 (1986) (in Japanese)

M. Okazaki, T. Endoh, T. Yada, T. Koizumi, Surface small crack growth behavior of sus304 stainless steel in low cycle fatigue under creep-fatigue condition at elevated temperature. J. Soc. Mat. Sci., Jpn. 36(410), 1232–1238 (1987) (in Japanese)

R. Ohtani, T. Kitamura, H. Murayama, N. Tada, Simulation of initiation and early propagation of creep-fatigue small cracks based on the model of random fracture resistance of grain boundaries. Trans. Jpn. Soc Mech. Eng. Ser. A, 54(503), 1312–1310 (1988) (in Japanese)

R. Ohtani, T. Kitamura, N. Tada, Numerical simulation of initiation and early propagation of creep-fatigue small cracks based on a model of random fracture resistance of grain boundaries, structural design for elevated temperature environments, ASME PVP, vol. 163, ed. by C. Becht, R. Ohtani, L.K. Severud, S.Y. Zamrik (ASME, New York, 1989), pp. 123–127

10.

N. Tada, T. Kitamura, R. Ohtani, Monte carlo simulation of creep-fatigue small cracks based on a three-dimensional model of random fracture resistance of grain boundaries. Trans. Jpn. Soc. Mech. Eng. Ser. A, 56(524), 708–714 (1990) (in Japanese)

11.

R. Ohtani, T. Kitamura, N. Tada, Stochastic simulation of initiation and growth of small surface cracks in creep-fatigue condition, in Proceeding of 4th International Conference on Fatigue and Fatigue Thresholds (Fatigue 90), Vol. IV (Materials and Component Engineering Pub., Birmingham, 1990), pp. 2143–2148

12.

T. Kitamura, N. Tada, M. Abe, M. Yumita, R. Ohtani, Effect of compression-going strain rate on initiation and growth of small cracks under creep-fatigue condition. Trans. Jpn. Soc. Mech. Eng. Sers. A, 56(523), 575–581 (1990) (in Japanese)

13.

N. Tada, Creep Fatigue Microcrack Initiation and Propagation in 304 Stainless Steel. Kyoto University Doctoral Dissertation (1992) (in Japanese)

14.

R. Ohtani, T. Kitamura, Creep-fatigue interaction under high-temperature conditions, in Handbook of Fatigue Crack Propagation in Metallic Structures, 2, ed. by C. Andrea, Elsevier, The Netherlands, pp. 1347–1383(1994).

15.

K. Tokimasa, Research on High-temperature Creep Fatigue of Heat-resistant Steel (Kyoto University Doctoral Dissertation, 1991) (in Japanese)

16.

H. Kawasaki, F. Ueno, K. Aoto, M. Ichimiya, Y. Wada, Evaluation of long term creep-fatigue life for type 304 stainless steel. J. Soc. Mat. Sci., Jpn. 41(471), 1773–1778 (1992) (in Japanese)

17.

W. Zhou, R. Ohtani, T. Kitamura, N. Tada, A. Kosaka, Creep-fatigue intergranular fracture of inner cracking type in type 304 stainless steel. J. Soc. Mat. Sci., Jpn. 44(496), 78–83 (1995) (in Japanese)

18.

T. Kitamura, R. Ohtani, N. Tada, W. Zhou, Characterization of creep-fatigue fracture of type 304 stainless steel based on initiation and growth of small cracks. Presented at the 1995 ASME/JSME Pressure Vessels and Piping Conference, “Mechanics and New Criteria for Life Assessment and Integrity Analysis” (Honolulu, Hawaii 1995)

19.

R. Ohtani, N. Tada, T. Hashimoto, Difference between monotonic tension and creep-fatigue in the behavior of small crack initiation and early growth of 304 stainless steel at elevated temperature. J. Soc. Mat. Sci., Jpn. 38(432), 89–94 (1989) (in Japanese)

20.

T. Kitamura, N. Tada, Y. Kuriyama, R. Ohtani, Distribution of grain-boundary length and inclination of type 304 stainless steel and its effects on small crack initiation and growth under creep-fatigue conditions. Trans. Jpn. Soc. Mech. Eng. Ser. A, 56(524), 702–707 (1990) (in Japanese)

21.

T.-J. Chuang, K.I. Kagawa, J.R. Rice, L.B. Sills, Non-equilibrium models for diffusive cavitation of grain interfaces. Acta Metall. 27(3), 265–284 (1979)CrossRef

22.

I.-W. Chen, A.S. Argon, Diffusive growth of grain-boundary cavities. Acta Metall. 29(10), 1759–1768 (1981)CrossRef

23.

R. Horiuchi, M. Otsuka, Mechanisms of intergranular fracture at high temperatures. Bullet. Jpn. Inst. Met. 22(4), 293–301 (1983) (in Japanese)

24.

N. Tada, R. Ohtani, T. Kitamura, M. Yamada, Inverse analysis on the distribution of internal small defects. Trans. Jpn Soc. Mech. Eng. Ser. A 59(558), 381–386 (1993) (in Japanese)

25.

R. Ohtani, Questions and solutions on the method of remaining-life evaluation of structural in high-temperature power plants. Trans. Jpn. Soc. Mech. Eng. Ser. A, 59(565), 2019–2026 (1993) (in Japanese)

26.

R. Ohtani, T. Kitamura, N. Tada, Cracking behavior of heat-resisting steels, alloys and a carbon-fibre-reinforced polymer at elevated temperatures. Mater. Sci. Eng.: A 143(1–2), 213–222 (1991)

27.

Report of the High Temperature Creep-Fatigue Testing Committee of the Iron and Steel Institute of Japan, Investigation of high temperature low-cycle fatigue properties of 18Cr-8Ni steel by strain range division (The Iron and Steel Institute of Japan, 1981) (in Japanese).

28.

F.C. Monkman and N.J. Grant, An empirical relationship between rupture life and minimum creep rate in creep-rupture tests. Proc. ASME 56, 593–620 (1956)

29.

S.S. Manson, Behavior of Materials Under Conditions of Thermal Stress (Proceedings of Heat Transfer Symposium, University of Michigan, 1953), pp.976–988

30.

L.F. Coffin Jr., A study of the effects of cyclic thermal stresses on a ductile metal. Trans. ASME 76, 931–949 (1954)

Titel: Conditions for Appearance of Internal Intergranular Cracking Type Fracture Under Creep-Fatigue
verfasst von: Weisheng Zhou
Naoya Tada
Junji Sakamoto
Verlag: Springer Nature Singapore
Buch: Creep-Fatigue Fracture: Analysis of Internal Damage
Print ISBN: 978-981-9718-78-8

Electronic ISBN: 978-981-9718-79-5

Copyright-Jahr: 2024
DOI: https://doi.org/10.1007/978-981-97-1879-5_3

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht